Sintered calcium aluminate refining slag
(calcium aluminate Synthetic slag for steelmaking)
Product Introduction
China Xingshi New Materials has developed and produced sintered calcium aluminate refining slag, which is suitable for removing impurities such as sulfur from molten steel during ladle refining.
Synthetic Slag performance
1. It does not absorb moisture, does not pulverize, and will not deteriorate during storage and transportation.
2. The mineral composition is basically the same as that of pre melted calcium aluminate
3. Low melting point, it can quickly melt in the ladle and play a role in desulfurization.
4. Can maintain good fluidity of port slag
Particle size:
1-30mm, 5-15mm, 1-10mm, 1-15mm, etc...
Physical and chemical indicators of Sintered Synthetic Slag
Model | CaO | Al2O3 | SiO2 | TiO2 | Fe2O3 | MgO | CaF2 |
XSSS-1 | 48-50 | 37-41 | 4-6 | ~2.5 | ~2.5 | 1.5~8.0 | - |
XSSS-2 | 42-45 | 42-45 | 4-6 | ~2.5 | ~2.5 | 1.5~8.0 | - |
XSSS-3 | 45-48 | 39-42 | 4-6 | ~2.5 | ~2.5 | 1.5~8.0 | - |
XSSS-4 | 32-35 | 50-53 | 8 | ~2.5 | ~2.5 | 1.5~8.0 | - |
**Please note: With the innovation and development of production technology, the content of some ingredients can be adjusted and controlled - Fluorine content, adjustable to low levels | |||||||
Sintered calcium aluminate refining slag
(calcium aluminate Synthetic slag for steelmaking)
Product Introduction
China Xingshi New Materials has developed and produced sintered calcium aluminate refining slag, which is suitable for removing impurities such as sulfur from molten steel during ladle refining.
Synthetic Slag performance
1. It does not absorb moisture, does not pulverize, and will not deteriorate during storage and transportation.
2. The mineral composition is basically the same as that of pre melted calcium aluminate
3. Low melting point, it can quickly melt in the ladle and play a role in desulfurization.
4. Can maintain good fluidity of port slag
Particle size:
1-30mm, 5-15mm, 1-10mm, 1-15mm, etc...
Physical and chemical indicators of Sintered Synthetic Slag
Model | CaO | Al2O3 | SiO2 | TiO2 | Fe2O3 | MgO | CaF2 |
XSSS-1 | 48-50 | 37-41 | 4-6 | ~2.5 | ~2.5 | 1.5~8.0 | - |
XSSS-2 | 42-45 | 42-45 | 4-6 | ~2.5 | ~2.5 | 1.5~8.0 | - |
XSSS-3 | 45-48 | 39-42 | 4-6 | ~2.5 | ~2.5 | 1.5~8.0 | - |
XSSS-4 | 32-35 | 50-53 | 8 | ~2.5 | ~2.5 | 1.5~8.0 | - |
**Please note: With the innovation and development of production technology, the content of some ingredients can be adjusted and controlled - Fluorine content, adjustable to low levels | |||||||